This paper presents the results of analytical studies concerning the flexuralstrengthening of reinforced concrete beams by external bonding of high-strength lightweightcarbon fiber reinforced plastic (CFRP) plates to tension face of the beam. Three groups of beamswere tested analytically and compared with existing experimental results. Results of the numericalanalyses showed that, although addition of CFRP plates to the tension face of the beam increasesthe strength, it decreases the beam ductility. Finite element modeling of fifteen different beams in aparametric study indicates that steel area ratio, CFRP thickness, CFRP ultimate strength andelastic modulus considerably influence the level of strengthening and ductility.

---

The aim of current study is to investigate the effect of Carbon Fiber Reinforced Polymer (CFRP) composites on the fatigue

response of reinforced concrete beams. 6 reinforced concrete (RC) beams from which 3 were retrofitted with CFRP sheets, were

prepared and subjected to fatigue load cycles. To predict and trace the failure occurrence and its growth, a small notch was

induced at the middle span in bottom surface of all RC specimens. At the certain points, strains in concrete and CFRP were

measured in each cycle. The upper limit of applied load was considered at the level of design service load of bridges. In addition,

strain measurements facilitated to the calculation of interfacial shear stresses between concrete substrate and the CFRP layer.

The variation of such stresses through load cycles has been presented and discussed. Also, a discussion on possibility of the local

debonding phenomenon resulted from such interfacial stresses was presented. Load–deflection curves, strain responses and

propagation of tensile cracks provided an insight on the performance of the CFRP strengthened beams subjected to different

cycles of fatigue loading. Variation of load-deflection curves through fatigue load cycles depicted stiffness degradation which

was discussed in the research.