Porous nanostructured SnO₂ with a sheet-like morphology was synthesized through a simple green substrate-free gelatin-assisted calcination process using Tin tetracholoride pentahydrate as the SnO₂ precursor and porcine gelatin as the template. Crystalline phase, morphology, microstructure, and optical characteristics of the as-prepared material were also investigated at different calcination temperatures using X-ray diffraction (XRD), Field emission scanning electron microscopy (FESEM), UV-visible absorption, and Photoluminescence spectroscopy (PL), respectively. XRD patterns of all the samples revealed the presence of a tetragonal crystalline structure with no other crystalline phases. Moreover, the synthesized hierarchical sheets assembled with nanoparticles displayed a large surface area and porous nanostructure. The calculated optical band gap energy varied from 2.62 to 2.87 eV depending on the calcination temperature. Finally, photoluminescence spectra indicated that the nanostructured SnO₂ could exhibit an intensive UV-violet luminescence emission at 396 nm, with shoulders at 374, violet emission peaks at 405 and 414 nm, blue-green emission peak at 486 nm, green emission peak at 534 nm and orange emission peak at 628 nm.

Keywords: SnO2, Porcine gelatin, Sheet-like morphology, Optical properties, Photoluminescence., Gel drying

Full-Text [PDF 2062 kb]   (6341 Downloads)    

Add your comments about this article : Your username or Email:

---

---