Amuei M, Emamy M, Khorshidi R, Akrami A. MICROSTRUCTURAL STUDIES OF Ti-REFINED Al2014 ALLOY PREPARED BY SIMA PROCESS. IJMSE 2015; 12 (3) :56-65
URL: http://ijmse.iust.ac.ir/article-1-830-en.html
URL: http://ijmse.iust.ac.ir/article-1-830-en.html
Abstract: (21979 Views)
In this study, Al2014 alloy refined with Al-5%Ti-1%B master alloy was prepared by strain-induced melt
activated (SIMA) process. The main variables of the SIMA process were cold working, holding time and temperature in
semi-solid state. Cold working was applied on specimens by upsetting technique to achieve 10%, 20% and 30% height
reduction. Cold worked specimens were heat treated in semi-solid state at 585 °C, 595 °C, 605 °C, 615 °C, 625 °C and
635 °C and were kept in these temperatures for different times (20 and 30 min). Observations through optical and
scanning electron microscopy were used to study the microstructural evaluation. The results revealed that fine and
globular microstructures are obtained by applying 30 % height reduction percentage and heat treating in 625 °C for
30 min. Comparison between refined and unrefined Al2014 alloy after applying SIMA process showed that Al-5%Ti-1%B master alloy has no significant effect on average globule size but makes the final structure more globular.
Type of Study: Research Paper |
Subject:
forming and mechanical properties
Send email to the article author
| Rights and permissions | |
 |
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License. |