S. Kord, M. H. Siadati, M. Alipour, H. Amiri, P.g. Koppad, A. C. Gowda,
Volume 15, Issue 4 (December 2018)
Abstract
The effects of rare earth element, erbium (Er) additions on the microstructure and mechanical properties of Al-15Zn-2.5Mg-2.5Cu alloy have been investigated. This new high strength alloy with erbium additions (0.5, 1.0, 1.5 and 2.0 wt%) was synthesized by liquid metallurgy route followed by hot extrusion. Microstructural characterization was performed using scanning electron microscope and electron probe microanalysis. Significant amount of grain refinement was observed with erbium addition in the hot extruded and heat treated alloy. Tensile test was performed to investigate the effect rare earth on mechanical behavior of alloy in as cast and hot extruded condition before and after T6 heat treatment. The combined effect of erbium addition, hot extrusion and heat treatment significantly enhanced the tensile strength of alloy (602 MPa) when compared to the as cast alloy without erbium addition (225 MPa). The strengthening of the alloy was attributed to grain refinement caused by erbium along with hot extrusion and formation of precipitates after T6 heat treatment. Fractograhic investigations revealed that the hot extruded alloy with erbium addition after heat treatment showed uniformly distributed deep dimples exhibiting ductile behavior.
Puneeth Puneeth, Gangarekaluve J. Naveen, Vishwanath Koti, Nitrahalli D. Prasanna, Litton Bhandari, Javaregowda Satheesh, Parthasarathy Sampathkumara,
Volume 19, Issue 1 (March 2022)
Abstract
Hybrid composite finds wide application in various fields. In this present study, the hybrid composites are developed using stir casting technique as per Taguchi’s L9 orthogonal array. Hybrid composites were fabricated using Aluminium Al6082 as the base material and reinforced with the combinations of reinforcements Al2SiO5 and B4C at three levels (4%, 8% and 12%).The developed composites were analyzed for micro structural investigations and mechanical tests were done as per ASTM standards. The micro structural analysis was done using optical Microscope and Scanning electron microscope while composition studies were done using X-ray diffraction and EDAX. Mechanical test like tensile, impact and flexural were conducted and their damage assessment was done using Scanning electron microscope. The fatigue characteristics like high cycle fatigue and fatigue crack propagation was studied both experimentally and numerically. The experimental data and numerical modeling analysis data obtained for the hybrid composite system, agree with each other.