Y. Fouad,
Volume 7, Issue 4 (10-2010)
Abstract
Abstract: Rotating bending fatigue tests have been performed using smooth specimens of a rolled AZ31 magnesium alloy in laboratory air at ambient temperature. Fatigue strength and characteristic was evaluated and fracture mechanism was discussed on the basis fracture surface analysis. Electrical polishing (EP) as well as deep rolling (ball burnishing (BB)) U-notched specimens were performed on two groups of samples, to evaluate optimum conditions for fatigue life. The microstructure and tensile properties of roll cast (RC) Mg- 3% Al- 1% Zn (AZ31) was investigated. The fatigue strength of 107 cycles around 100 MPa for deep rolling while it was around 40 MPa for Electrical polishing. It was very important to understand the effect of (ball burnishing (BB)) conditions on the hardness of the surface through to the core. The two procedures improved the fatigue performance, but better improve in results were found in ball burnishing. The growth of small cracks initiated at the surface coincided with the FCP characteristic after allowing for crack closure for large cracks, but the operative fracture mechanisms were different between small and large cracks. At the subsurface crack initiation site, smooth facets were always present regardless of applied stress level.
A. Khalili, M. Mojtahedi, M. Goodarzi, M. J. Torkamani,
Volume 16, Issue 3 (9-2019)
Abstract
The aim of this work was to synthesize TiC reinforced coating on carbon steel via reduction of ilmenite powder. A mixture of ilmenite and graphite was pre-placed on AISI 1020 steel surface. The effect of the addition of excess graphite amounts on the progress of synthesis of carbide particles was studied. The evolution of phases in different coatings was analysed via X-ray diffraction and scanning electron microscopy. Then again, the initial powder mixtures were mechanically activated for various durations, to accelerate the reactions in transient melt pool. Finally, the Fe-TiC hard coating was successfully synthesized by carbothermic reduction of ilmenite through laser surface treatment. Moreover, it is proved that combination of mechanical activation with additive laser melting effectively improves the level of ilmenite reduction, besides enhancing the distribution of hard particles and the hardness of the coatings to more than 1300 HV.