Iranian Journal of Materials Science and Engineering

In this study the effect of nano meter size ZrO₂ particles on the microstructure, densification and hydration resistance of magnesite –dolomite refractories was investigated. 0, 2, 4, 6 and 8 wt. % ZrO₂ particles that were added to magnesite –dolomite refractories containing 35 wt. % CaO. The Hydration resistance was measured by change in the weight of specimens after 72 h at 25℃ and 95% relative humidity. The results showed with addition of nano meter size ZrO₂ particles_, the lattice constant of CaO increased, and the bulk density and hydration resistance of the specimens increased while apparent porosity decreased. With the addition of small amount ZrO₂ the formation of CaZrO₃ phase facilitated the sintering and the densification process. The mechanism of the nano meter size ZrO₂ particles promoting densification and hydration resistance is decreasing the amount of free CaO in the specimens.